W1a Poe | Foshan Silicone Group

Basic Info.

Model NO.	W1A
Specification	20 KGs per bag
Trademark	Colebond
Origin	China
HS Code	3901909000
Production Capacity	20000 Tons Per Year

Product Description

Product description
W1A is prepared by grafting MAH by POE reaction. Since it introduces a strongly polar side group (MAH) on the main chain of POE molecule, MAH grafted POE can become a polar material. A bridge for adhesion and compatibility with non-polar materials. In the application of nylon + glass fiber modification, it can react with the glass fiber after surface treatment to improve the compatibility of nylon and glass fiber, thereby improving the tensile strength and impact strength of nylon. W1A can be used as both a compatibilizer and a toughening agent. As a nylon compatibilizer, it is also suitable for PA/PE and PA/PP alloys, which can improve the toughness of the alloy. As a nylon toughening agent, its low temperature The performance is very superior, the impact strength of PA6+15%W1A at -40ºC can be maintained at 35-40% of the impact at room temperature.

Product models	W1A	W1A-2
Melting index	0.3-1.0	0.3-1.0
Grafting rate	High	High
density	0.87g/cm³	0.87g/cm³
performance	PA reinforced filling, ultra-low temperature toughening	PA reinforced filling, ultra-low temperature toughening
Typical application(advantages)	Application: Be used for PA6 or PA66 compatibilizing or toughening. Increase the impact resistance and processability of nylon,decrease the water absorption,greatly improve the cold-resistance. Be used for the compatibilizer of nylon and polypropylene/polyethylene alloy. Be used for the macromolecular modifier(couling agent)of mineral-filled or grass-flber-filled nylon.	Application:1.Be used for PA6 or PA66 compatibilizing or toughening. Increase the impact resistance and processability of nylon,decrease the water absorption,greatly improve the cold-resistance.2.Be used for the compatibilizer of nylon and polypropylene/polyethylene alloy.3.Be used for the macromolecular modifier(couling agent)of mineral-filled or grass-flber-filled nylon.
Applied areas	Ski board, nylon cable tie	Ski board, nylon cable tie

NOTE: The above data are typical test values and should not be interpreted as a specification low < 0.4wt %, medium 0.4-0.8 wt%, high > 0.8wt%.
Comparison parameters of different applications
Table1:Typical Data of Toughening of PA6 Resin

Performance	Unit	PA6	PA6+15%W1A	PA6+20%W1A
Tensile strength	MPa	60	55	45
Flexural strength	MPa	90	80	70
Lzod notched impact strength (23ºC)	J/m	80	600	800

Table2:Typical Data of Toughening of PA66 Resin

Performance	Unit	PA66	PA66+15%W1A	PA66+20%W1A
Tensile strength	MPa	75	53	47
Flexural strength	MPa	102	59	55
Lzod notched impact strength (23ºC)	J/m	80	600	1000

NOTE:The above data are typical experimental values, for reference only, the viscosity of PA6 used in Table 1 is 2.8, and the viscosity of PA66 used in Table 2 is 2.7.
Table3:Typical Data of Reinforcing and Toughening of PA6 Resin

Performance	Unit	PA6	PA6+30%GF+6%W1A
Tensile strength	MPa	60	135
Flexural strength	MPa	90	195
Lzod notched impact strength (23ºC)	J/m	80	250

Table4:Typical Data of Reinforcing and Toughening of PA66 Resin

Performance	Unit	PA66	PA6+30%GF+6%W1A
Tensile strength	MPa	75	150
Flexural strength	MPa	102	215
Lzod notched impact strength (23ºC)	J/m	80	200

NOTE: The above data are typical experimental values, for reference only, the viscosity of PA6 used in Table 3 is 2.8, and the viscosity of PA66 used in Table 4 is 2.7. NOTE: The data above are all experimental typical values, only for reference.
Suggested dose: The dose (5-25%) may be increased or decreased properly according to the toughness requirements and by taking the cost into consideration.3-10% shall be adopted for PA6/PA66 reinforcing and toughening, while 5% shall be adopted for the compatibilizer of nylon and polypropylene/polyethylene alloy.
Packaging, storage and transportation: 20kg kraft bag with internal plastic bag. This product shall be treated as non-hazardous article and be stored or transported under dry conditions, and sunlight and rain shall be avoided.Products of the same series

Model	Melt index	Grafting ratio	Density(g/cm3)	Characteristic
W1A	0.3-1.0	High	0.87	PA reinforced filling, ultra-low temperature toughening
W1A-2	0.3-1.0	High	0.87	PA reinforced filling, ultra-low temperature toughening
W1A-4	0.1-1.0	High	0.87	PA reinforced filling, ultra-low temperature toughening
W1A-6	>0.1	High	0.89	PA reinforced filling,low temperature toughening
W1A-F	5-14	High	0.87	PA reinforced filling,TPE encapsulated
W1B	0.3-2.0	High	0.87	PA reinforced filling, ultra-low temperature toughening
W1	0.2-1.0	High	0.88	PA reinforced filling,low temperature toughening
W1C	0.3-1.5	Middle	0.88	PA reinforced filling,low temperature toughening
W1D	0.6-2.0	High	0.88	PA reinforced filling,low temperature toughening
W1F	10-24	High	0.87	PA enhanced filling, high dispersion

Application display

5.Delivery on time and global service.

W1a Poe-G-mAh/mAh Grafted Poe Used as Compatibilizer Toughening Agent for Polyamides/ Nylon/PA Glass Fiber